A general and low-cost synthetic route to high-surface area metal oxides through a silica xerogel template Original Research Article

Porous metal oxides with a large surface area are synthesised by means of a procedure based on the templating approach. An inexpensive porous silica xerogel synthesised at moderate temperatures (∼100 °C) in order to preserve the silanol superficial groups was used as template. In a first step, the silica porosity was filled with a concentrated solution containing a metallic salt. Then, the impregnated sample was calcined in air at a temperature of 600 °C. Under these conditions, the metal oxides were synthesised within the confined space provided by the silica pores. Finally, the product was recovered after dissolution of the silica framework in 2 M NaOH solution. The materials obtained by this procedure are made up of aggregates of nanoparticles and/or 3D solid structures containing confined pores. In this work, the synthetic route proposed is illustrated by the preparation of various binary metal oxides (i.e. Fe2O3, Cr2O3, NiO, CeO2, Mn2O3, Co2O3 and Al2O3). The BET surface areas measured for these materials are in the range of 100–270 m2 g−1. The proposed method is not restricted to the binary metal oxides. It can also be used in the preparation of other inorganic materials such as metal sulphides or mixed metal oxides.