The structure and optical properties of AlN nanocrystals prepared by Schlenk techniques at atmospheric pressure and low temperature Original Research Article

AlN nanocrystals were prepared in organic solvent at atmospheric pressure and low temperature by the Schlenk technique. Both hexagonal and cubic AlN nanocrystals were obtained. The hexagonal nano-AlN powder possessed a wurtzite structure with a=3.124 Å, c=5.024 Å, the average grain size was about 2 nm. The lattice constant of the cubic nano-AlN was a=9.171 Å, the average grain size was about 4 nm. The structural and optical properties of the obtained AlN were analyzed. The emission related to deep-level defects was investigated by using temperature-dependent photoluminescence.