Nanocrystalline Sr2FeMoO6 prepared by citrate-gel method Original Research Article

Double perovskite Sr2FeMoO6 powders with small crystallite size have been synthesised with citrate-gel method. The starting solution pH was varied between 1.5 and 9.0 resulting in large differences in the phase composition and ordering of B′/B″B′/B″ sites. The samples prepared at 975 °C had crystallite sizes under 40 nm whereas crystallite sizes of the samples prepared at 1050 °C were between 78 and 239 nm. The XRD patterns were refined with spacegroup I 4/m, which gave good results for both batches, although clearly better results were obtained with monoclinic P 21/n spacegroup for the 975 °C batch. The ordering and the saturation magnetization agreed well with each other after treatment at 1050 °C, but the samples prepared at 975 °C had a strongly reduced saturation magnetization from that given by the ordering.