Abstract :
Lithium haloborate glasses have been prepared according to the formula (70−y)B2O3–30BaF2–yLiX where y=0, 5, 10, 15 and 20 mol% and X=F, Cl and Br. The UV absorption spectra have been recorded at room temperature. The optical energy band gap Eopt and Urbach energy Etail was determined. Increasing concentration of LiX in the glass shifts the UV cutoff to lower energy and decreases both Eopt and Etail. The shift in UV cutoff and the decrease of Eopt and Etail are maximum in the range 0–5 mol% LiX. The decrease of Eopt increases going from F, Cl to Br, whereas the decrease of Etail increases going from Br, Cl to F. At higher LiX concentrations Urbach energy Etail increases again. The behavior of Eopt has been correlated with the B–O bond length of the studied glasses. The decrease of Eopt and Etail is due to the increase of nonbridging oxygen (NBO) concentration with increase of LiX content. The increase of Etail at higher concentrations is attributed to the halide ion accumulation in the interstitial positions and to the formation of orthoborate groups. Refractive index, which is measured and calculated, molar refraction and polarizability are all correlated with the composition of the glasses.