EPR study of nitrogen-doped mesoporous TiO2 powders Original Research Article

Mesoporous titanium dioxide powders were synthesized by the sol–gel route either directly or using the P123 templating agent and nitrogen doping from thiourea. X-ray diffraction studies show that doping and structuring give rise to rutile growth at a relatively low temperature of 400 °C compared to the transition point of pure TiO2, which is close to 900 °C. Systematic EPR experiments were performed in order to monitor the involved paramagnetic centres with respect to calcination treatments and also to probe the nitrogen doping efficiency in the host media. Several paramagnetic species were found in these mesostructured samples mainly with oxygen radicals for calcinations at 400 °C, while nitrogen centres appear for calcination temperature as high as 500 °C. The effect of material microstructure on the effective incorporation of nitrogen in the TiO2 lattice is also examined and compared in representative samples.