Synthesis, structural and electrical properties of La and Nb modified Bi4Ti3O12 ferroelectric ceramics Original Research Article

Polycrystalline ceramic samples of Bi4−xLaxTi3O12 (x=0.0, 0.5 and 1) and Bi3.5La0.5Ti3−yNbyO12 (y=0.02 and 0.04) have been synthesized by standard high temperature solid state reaction method using high purity oxides and carbonates. The effect of lanthanum doping on Bi-site and Nb doping on Ti-site on the structural and electrical properties of Bi4Ti3O12 powders was investigated by X-ray diffraction, scanning electron microscopy, dc conductivity and dielectric studies. A better agreement between the observed and calculated X-ray diffraction pattern was obtained by performing the Rietveld refinement with a structural model using the non-centrosymmetric space group Fmmm in all the cases. A better agreement between observed and calculated d-values also shows that the lattice parameters calculated using the Rietveld refinement analysis are better. The increase in lanthanum and niobium contents does not lead to any secondary phases. It is found that La3+ doping reduces the material grain size and changes its morphology from the plate-like form to a spherical staking like form. The substitution of Nb for Ti ions affected the degree of disorder and modified the dielectric properties leading to more resistive ceramic compounds. The shape and size of the grains are strongly influenced by the addition of niobium to the system. The activation energies of all the compounds were calculated by measuring their dc electrical conductivities. The frequency and temperature dependent dielectric behavior of all the compounds have also been studied and the results are discussed in detail. The substitution of La and Nb on the Bi and Ti sites decreased the Tc and improved the dielectric and ferroelectric behavior.