Preparing nanometer scaled Tb-doped Y2O3 luminescent powders by the polyol method

Sub-micrometer Tb-doped Y2O3 luminescent powders were prepared from nitrate precursors using the polyol method. Just after precipitation, the powders consist of agglomerates with a spherical shape and a size ranging between 400 and 500 nm. Each agglomerate is composed of ultra-small crystallites (from 3 to 6 nm) of a bcc oxide phase whose luminescence presents original features in comparison with bulk materials. Powders were further calcinated at different temperatures and for annealing below 900 °C, highly crystalline samples with the classical green 5D4→7F5 luminescent transitions of Tb3+ ions are obtained. For optimized annealing temperatures, sintering between the agglomerates is avoided and a sub-micrometric powder with a narrow size distribution and a high luminescence is obtained.