Synthesis of nanocrystals in KNb(Ge,Si)O5 glasses and chemical etching of nanocrystallized glass fibers

The nanocrystallization behavior of 25K2O−25Nb2O5–(50−x)GeO2–xSiO2 glasses with image (i.e., KNb(Ge,Si)O5 glasses) and the chemical etching behavior of transparent nanocrystallized glass fibers have been examined. All glasses show nanocrystallization, and the degree of transparency of the glasses studied depends on the heat treatment temperature. Transparent nanocrystallized glasses can be obtained if the glasses are heat treated at the first crystallization peak temperature. Transparent nanocrystallized glass fibers with a diameter of about 100 μm in 25K2O–25Nb2O5–50GeO2 are fabricated, and fibers with sharpened tips (e.g., the taper length is about 450 μm and the tip angle is about 12°) are obtained using a meniscus chemical etching method, in which etching solutions of 10 wt%-HF/hexane and 10 M-NaOH/hexane are used. Although the tip (aperture size) has not a nanoscaled size, the present study suggests that KNb(Ge,Si)O5 nanocrystallized glass fibers have a potential for new near-field optical fiber probes with high refractive indices of around image and high dielectric constants of around image (1 kHz, room temperature).