An alternative manufacturing route has been developed for cobalt triantimonide and magnesium disilicide derivatives. Elemental powders were mixed in stoichiometric proportions, cold pressed into cylindrical preforms and heated in oxygen-free environment to initiate the exothermic reaction. According to DTA/TG measurements and observations under high-temperature microscope, the onset of reaction occurred at a temperature not exceeding the melting point of the more volatile component, i.e. antimony in the case of CoSb3 and magnesium in the case of Mg2Si. The reaction products were additionally heat treated to secure homogenization. Dense sinters were obtained by hot uniaxial pressing of the obtained powders in moderate temperature-and-pressure conditions. Several advantages were identified in the proposed technology: absence of liquid phases, relatively short time of the synthesis, possibility of in-situ or ex-situ doping and grain size control.