Narrow spectral emission CaMoO4: Eu3+, Dy3+, Tb3+ phosphor crystals for white light emitting diodes

Alkaline earth metal molybdates are promising candidates as a host material for high efficiency narrow spectral emission phosphors. These phosphors could potentially be used for the fabrication of phosphor-converted light emitting diodes (pc-LEDs). Phosphor crystals of calcium molybdate doped with rare earth dopant Ln3+(Ln=Eu, Dy, Tb) grown using flux growth method have been shown to exhibit higher excitation efficiency than the powders synthesized by solid-state reaction process. Molybdenum (VI) oxide has been found to be a suitable flux for growing large size optically transparent high quality crystals at a temperature around 1100 °C. Using the excitation wavelengths of 465 nm, 454 nm and 489 nm for CaMoO4: Eu3+, CaMoO4: Dy3+ and CaMoO4: Tb3+, respectively, intense emission lines at wavelengths of 615 nm, 575 nm and 550 nm were observed. The optimized doping concentrations of 12%, 2% and 5% for Eu3+, Dy3+ and Tb3+, respectively, provided the highest luminescence intensity.