Lattice crossover and phase transitions in NdAlO3–GdAlO3 system

Phase and structural behaviour in the (1−x )NdAlO3–x GdAlO3 system in a whole concentration range has been studied by means of in situ high-resolution X-ray synchrotron powder diffraction technique and differential thermal analysis. Two kinds of solid solutions Nd1−xGdxAlO3 have been found at room temperature: one with rhombohedral (x <0.15) and one with orthorhombic (x ≥0.20) symmetry. A morphotropic phase transition occurs at x ≈0.15, where the co-existence of both phases was observed. Peculiarity of the orthorhombic solid solution is the lattice parameter crossover at the compositions with x =0.33, 0.49 and 0.62. First-order structural transition Pbnm ↔R View the MathML source3¯с has been detected both from in situ powder diffraction and thermal analysis data. Continuous phase transformation R View the MathML source3¯с ↔Pm View the MathML source3¯m above 2140 K has been predicted for Nd-rich sample Nd0.85Gd0.15AlO3 from the extrapolation of high-temperature behaviour of the lattice parameter ratio of the rhombohedral phase. Based on the experimental data, the phase diagram of the pseudo-binary system NdAlO3–GdAlO3 has been constructed.