Author/Authors :
B.S.Rodchenkov، نويسنده , , B.S and Prokhorov، نويسنده , , V.I and Makarov، نويسنده , , O.Yu and Shamardin، نويسنده , , V.K and Kalinin، نويسنده , , G.M and Strebkov، نويسنده , , Yu.S and Golosov، نويسنده , , O.A، نويسنده ,
Abstract :
The main options for the manufacturing of high heat flux (HHF) components is hot isostatic pressing (HIP) using either solid pieces or powder. There was no database on the radiation behaviour of these materials, and in particular stainless steel (SS) 316L(N)-IG with ITER components manufacturing thermal cycle. Irradiation of wrought steel, powder-HIP, solid-HIP and HIPed joints has been performed within the framework of an ITER task. Specimens cut from 316L(N)-IG plate, HIP products, and solid-HIP joints were irradiated in the SM-3 reactor in Dimitrovgrad up to 4 and 10 dpa at 175°C and 265°C. The paper describes the results of post-irradiation tensile and fracture toughness tests.