TEM and PAS study of neutron irradiated VVER-type RPV steels

Conventional transmission electron microscopy and positron lifetime and Doppler broadening positron annihilation spectroscopy techniques have been used to investigate the radiation-induced microstructural changes in surveillance specimens of VVER-type reactor pressure vessel (RPV) steels, and RPV steels irradiated in the research reactor. Defects visible in transmission electron microscopy consist of black dots, dislocation loops and precipitates concentrated along the dislocation substructure. Their size and density depend on the neutron flux and fluence. The parallel set of thermally aged specimens, specimens recovery annealed after irradiation and specimens irradiated in a lower neutron flux was investigated too. No defects discernible in transmission electron microscopy were found after accelerated irradiation in the research reactor. In addition to visible defects, the small-volume vacancy clusters were identified by positron annihilation spectroscopy.