Author/Authors :
Ioltukhovskiy، نويسنده , , A.G and Leonteva-Smirnova، نويسنده , , M.V and Solonin، نويسنده , , M.I. and Chernov، نويسنده , , V.M and Golovanov، نويسنده , , V.N and Shamardin، نويسنده , , V.K and Bulanova، نويسنده , , T.M. and Povstyanko، نويسنده , , A.V. and Fedoseev، نويسنده , , A.E، نويسنده ,
Abstract :
Heat resistant 12% Cr steels of the 16Cr12W2VTaB type (12Cr-2W-V-Ta-B-0.16C) provide a reduced activation material that can be used as a structural material for fusion and fast breeder reactors. The composition under study meets scientific and engineering requirements and has an optimal base element composition to provide a δ-ferrite content of no more than 20%. It also has a minimum quantity of low melting impurity elements and non-metallic inclusions. Short-term tensile properties for the steel tested to 700 °C are provided after the standard heat treatment (normalization, temper). Rupture strength and creep properties for the steel depending on the initial heat treatment conditions are also given. The microstructural stability of the 16Cr12W2VTaB type steel at temperatures up to 650 °C is predicted to be good, and the properties of the steel after irradiation in BOR-60 are demonstrated.