Effects of fibers and fabrication processes on mechanical properties of neutron irradiated SiC/SiC composites

Radiation effects on flexural properties of SiC/SiC composites fabricated by forced thermal gradient chemical vapor infiltration (F-CVI) process, reaction sintered (RS) process and polymer impregnation and pyrolysis (PIP) process were investigated. In this study, neutron irradiation at 1073 K up to 0.4×1025 n/m2 (E>0.1 MeV) was performed. For F-CVI and RS SiC/SiC, due to the irradiation damage of interphase like pyrolytic carbon and boron nitride, which were sensitive to neutron irradiation, composite stiffness was slightly decreased. On the contrary, for PIP SiC/SiC, there was no significant change in stiffness before and after irradiation. Composite strength, however, was nearly stable against high-temperature irradiation with such a low fluence, except for RS SiC/SiC, since mechanical characteristics of fiber and matrix themselves were still stable to neutron irradiation. However RS SiC/SiC had a slight reduction of flexural strength due to the severe degradation of the interface by neutron irradiation.