Effect of post-weld heat treatment on the mechanical properties of electron beam welded joints for CLAM steel

In this paper the microstructure and mechanical properties of electron beam weld (EBW) joints for China low activation martensitic (CLAM) steel, which underwent a series of different post weld heat treatments (PWHTs) were studied. The aim of the study was to identify suitable PWHTs that give a good balance between strength and toughness of the EBW joints. The microstructural analyses were performed by means of optical microscope (OM) and scanning electron microscope (SEM). The mechanical properties were determined via tensile tests and Charpy impact tests. The results showed that the tensile strength of the as-weld joint (i.e. without any PWHT) were close to that of the base metal, but the impact toughness was only 13% of that of the base metal due to the existence of a delta-ferrite microstructure. To achieve a significant improvement in toughness a PWHT needs to be performed. If a one-step PWHT is applied tempering at 760 °C for 2 h gives EBW joints with high strength at a still acceptable toughness level. If a two-step PWHT is applied, a process involving quenching at 980 °C for 0.5 h followed by tempering at 740 °C or 760 °C for 2 h gives EBW joints with high strength and toughness properties. Whenever possible a two-step PWHT should be applied in favor of a one-step process, because of higher resulting strength and toughness properties.