Interdiffusion behaviors in doped molybdenum uranium and aluminum or aluminum silicon dispersion fuels: Effects of the microstructure

Si addition to Al is considered as a promising route to reduce (U,Mo)–Al interaction kinetics, due to its accumulation in the interaction layer, yielding the formation of silicide phases. The (U,Mo) alloy microstructure, and especially its homogenization state, could play a role on this accumulation process. The addition of a third element in γ(U,Mo) could also influence diffusion mechanisms of Al and Si. These two parameters were studied by means of diffusion couple experiments by joining γU based alloys with Al and (Al,Si) alloy. al elements X added into γ(U,Mo) were thoroughly chosen on the following criteria: (i) the potential solubility of the alloying element into the γ(U,Mo) matrix, (ii) its capability to form the ternary aluminides based on the CeCr2Al20 and Ho6Mo4Al43 – types, and (iii) the feasibility to control the microstructure of the alloys. On this basis, a test matrix is defined. It concerns γ(U80,Mo15,X5) alloys (in at.%) with X = Y, Cu, Zr, Ti or Cr. These alloys were homogenized and coupled with Al or (Al,Si) alloy. s evidenced, first, the importance of the state of homogenization of the γ(U,Mo) binary alloy on interaction processes with (Al,Si) alloy, and the benefit on the diffusion of Si through the interaction layer, as observed on the elementary concentration profiles, when the third element X has some solubility into γ(U,Mo) alloy.