Mechanisms of stress relief cracking in titanium stabilised austenitic stainless steel

The heat affected zone (HAZ) of AISI 321 welds may exhibit a serious form of cracking during service at high temperature. This form of damage, called ‘stress relief cracking’, is known to be due to work hardening but also to aging due to Ti(C,N) precipitation on dislocations which modifies the mechanical behaviour of the HAZ. The present study aims to analyse the latter embrittlement mechanism in one specific heat of 321 stainless steel. To this end, different HAZs are simulated using an annealing heat-treatment, followed by various cold rolling and aging conditions. Then, we study the effects of work hardening and aging on Ti(C,N) precipitation, on the mechanical (hardness, tensile and creep) behaviour of the simulated HAZs and on their sensitivity to intergranular crack propagation through stress relaxation tests performed on pre-cracked CT type specimens tested at 600 °C. It is shown that work hardening is the main parameter of the involved mechanism but that aging does not promote crack initiation although it leads to titanium carbide precipitation. Therefore, the role of Ti(C,N) precipitation on stress relief cracking mechanisms is discussed. An attempt is made to show that solute drag effects are mainly responsible for this form of intergranular damage, rather than Ti(C,N) precipitation.