High heat flux test with HIP-bonded Ferritic Martensitic Steel mock-up for the first wall of the KO HCML TBM

In order for a Korean Helium Cooled Molten Lithium (HCML) Test Blanket Module (TBM) to be tested in the International Thermonuclear Experimental Reactor (ITER), fabrication method for the TBM FW such as Hot Isostatic Pressing (HIP, 1050 °C, 100 MPa, 2 h) has been developed including post HIP heat treatment (PHHT, normalizing at 950 °C for 2 h and tempering at 750 °C for 2 h) with Ferritic Martensitic Steel (FMS). Several mock-ups were fabricated using the developed methods and one of them, three-channel mock-up, was used for performing a High Heat Flux (HHF) test to verify the joint integrity. Test conditions were determined using the commercial code, ANSYS-11, and the test was performed in the Korea Heat Load Test (KoHLT) facility, which was used a radiation heating with a graphite heater. The mock-up survived up to 1000 cycles under 1.0 MW/m2 heat flux and there is no delamination or failure during the test.