Hydrogen permeation characteristics of La27Mo1.5W3.5O55.5

Hydrogen permeation in 30% Mo-substituted lanthanum tungsten oxide membranes, La27Mo1.5W3.5O55.5 (LWMo), has been measured as a function of temperature, hydrogen partial pressure gradient, and water vapor pressure in the sweep gas. Transport of hydrogen by means of ambipolar proton–electron conductivity and – with wet sweep gas – water splitting contributes to the measured hydrogen content in the permeate. At 700 °C under dry sweep conditions, the H2 permeability in LWMo was image mL min−1 cm-1, which is significantly higher than that for state-of-the-art SrCeO3-based membranes. Proton conductivity was identified as rate limiting for ambipolar bulk transport across the membrane. On these bases it is evident that Mo-substitution is a successful doping strategy to increase the n-type conductivity and H2 permeability compared to nominally unsubstituted lanthanum tungsten oxide. A steady-state model based on the Wagner transport theory with partial conductivities as input parameters predicted H2 permeabilities in good agreement with the measured data. LWMo is a highly competitive mixed proton–electron conducting oxide for hydrogen transport membrane applications provided that long term stability can be ensured.