Pitting corrosion of the laser surface melted Alloy 600

The effect of laser surface melting (LSM) on the resistance to pitting corrosion of Ni-base Alloy 600 was investigated by a potentiodynamic polarization test in 1 M NaCl solutions at pH values of 4 and 10 at temperatures of 30, 60 and 90 °C. The pitting potentials of Alloy 600 were markedly increased by the LSM process, when compared with those of the non-laser treated Alloy 600. From the microscopic examination after the corrosion test, it was found that the pitting was initiated at the junction between a TiN inclusion and the matrix, possibly at the site of a sulfide physically associated with the TiN inclusion. The homogeneous micro-structure associated with the reduction of the inclusion size during the LSM process could be attributed to the improvement of the pitting corrosion properties in the LSM Alloy 600.