Oxygen potential of (U0.88Pu0.12)O2±x and (U0.7Pu0.3)O2±x at high temperatures of 1673–1873 K

The oxygen potential of (U0.88Pu0.12)O2±x (−0.0119 < x < 0.0408) and (U0.7Pu0.3)O2±x (−0.0363 < x < 0.0288) was measured at high temperatures of 1673–1873 K using gas equilibrium method with thermo gravimeter. The measured data were analyzed by a defect chemistry model. Expressions were derived to represent the oxygen potential based on defect chemistry as functions of temperature and oxygen-to-metal ratio. The thermodynamic data, Δ G ¯ O 2 , Δ H ¯ O 2 and Δ S ¯ O 2 , at stoichiometric composition were obtained. The expressions can be used for in situ determination of the oxygen-to-metal ratio by the gas-equilibration method. The calculation results were consistent with measured data. It was estimated that addition of 1 wt.% Pu content increased oxygen potential of uranium and plutonium mixed oxide by 2–5 kJ/mol.