Analysis of water radiolysis in relation to stress corrosion cracking of stainless steel at high temperatures – Effect of water radiolysis on limiting current densities of anodic and cathodic reactions under irradiation

Electrochemical corrosion potential (ECP) is an important measure for environmental factor in relation to stress corrosion cracking (SCC) of metal materials. In the case of SCC for in-core materials in nuclear reactors, radiolysis of coolant water decisively controls ECP of metal materials under irradiation. In the previous models for ECP evaluation of stainless steel, radiolysis of reactor water in bulk was considered to calculate the bulk concentrations of the radiolysis products. In this work, the radiolysis not only in bulk but also in the diffusion layer at the interface between stainless steel and bulk water was taken into account in the evaluation of ECP. The calculation results shows that the radiolysis in the diffusion layer give significant effects on the limiting current densities of the redox reactions of the radiolysis products, H2O2 and H2, depending on dose rate, flow rate and water chemistry, and leads to the significant increase in the ECP values in some cases, especially in hydrogen water chemistry conditions.