Phase characteristics of a number of U–Pu–Am–Np–Zr metallic alloys for use as fast reactor fuels

Metallic fuel alloys consisting of uranium, plutonium, and zirconium with minor additions of americium and neptunium are under evaluation for potential use to transmute long-lived transuranic actinide isotopes in fast reactors. A series of test designs for the Advanced Fuel Cycle Initiative (AFCI) have been irradiated in the Advanced Test Reactor (ATR), designated as the AFC-1 and AFC-2 designs. Metal fuel compositions in these designs have included varying amounts of U, Pu, Zr, and minor actinides (Am, Np). Investigations into the phase behavior and relationships based on the alloy constituents have been conducted using X-ray diffraction and differential thermal analysis. Results of these investigations, along with proposed relationships between observed behavior and alloy composition, are provided. In general, observed behaviors can be predicted by a ternary U–Pu–Zr phase diagram, with transition temperatures being most dependent on U content. Furthermore, the enthalpy associated with transitions is strongly dependent on the as-cast microstructural characteristics.