Deuterium retention in tungsten at fluences of up to 1026 D+/m2 using D+ ion beams

Deuterium retention in two types of polycrystalline tungsten (PCW) was studied as a function of incident ion fluence, ion energy, and specimen temperature. (i) D retention at 300 K, as a function of D+ fluence, demonstrated a trend to saturation in both the Rembar hot-rolled thin foil and Plansee tungsten plate. At 500 K, new D retention results for the Plansee PCW showed an increasing trend with increasing incident D+ fluence without any indication of saturation, in agreement with previous results for Rembar PCW [A.A. Haasz, J.W. Davis, M. Poon, R.G. Macaulay-Newcombe, J. Nucl. Mater. 258–263 (1998) 889–895]. Even when the incident D+ fluence was increased to 8 × 1025 D+/m2, which is in the fluence range of plasma devices, there was still no sign of saturation. (ii) The temperature dependence results for the Plansee PCW show a decreasing trend in D retention as the temperature is increased from 300 to 500 K. These results differ from previous studies of Rembar PCW [A.A. Haasz, J.W. Davis, M. Poon, R.G. Macaulay-Newcombe, J. Nucl. Mater. 258–263 (1998) 889–895], but are similar to those seen for single crystal tungsten [M. Poon, A.A. Haasz, J.W. Davis, R.G. Macaulay-Newcombe, J. Nucl. Mater. 313–316 (2003) 199]; an explanation for the different behaviour is suggested. (iii) Varying the D+ energy from 100 to 500 eV/D+ plays a minor role in the amount of D retained, suggesting that D retention in W depends more on the W structure, incident ion fluence and specimen temperature, rather than on the incident ion energy when the energy is below the threshold for damage formation (∼960 eV for D on W).