The effect of radiation on the anaerobic corrosion of steel

To ensure the safe encapsulation of spent nuclear fuel elements for geological disposal, SKB of Sweden are considering using a canister, which consists of an outer copper canister and a cast iron insert. Previous work has investigated the rate of gas generation due to the anaerobic corrosion of ferrous materials over a range of conditions. This paper examines the effect of radiation on the corrosion of steel in repository environments. Tests were carried out at two temperatures (30 °C and 50 °C), two dose rates (11 Gray h−1 and 300 Gray h−1) and in two different artificial groundwaters, for exposure periods of several months. Radiation was found to enhance the corrosion rate at both dose rates but the greatest enhancement occurred at the higher dose rate. The corrosion products were predominantly magnetite, with some indications of unidentified higher oxidation state corrosion products being formed at the higher dose rates.