Experimental investigation of helium migration in an fcc aluminum matrix

Experimental investigation of helium migration in an fcc aluminum is reported. A pure aluminum with 0.15 wt% of 10B was neutron-irradiated to obtain (1.2 ± 0.2) × 1024 m−3 helium atoms in the metal according to the reaction 10B + n → 7Li + 4He. The post-irradiated metal was observed in situ in TEM while the sample was heated to 470 °C with a hot stage holder. um-rich area was found in the vicinity of nanometric 10B segregates that were not solute in the aluminum. The helium-rich area was characterized as a polygonal faceted region. According to EELS measurements, this area is saturated with NHe = (3 ± 1) × 1028 m−3 helium atoms, which are (30–65)% of the atoms in the observed area. found that the helium-rich area expands due to helium migration. Electron beam diffraction revealed that the preferred orientation of the helium atoms’ migration is normal to plane ( 0 2 ¯ 2 ) . The results are consistent with models for helium atoms migration between interstitial sites for an fcc metal.