Tokamak and laboratory modeling of hydrocarbon film deposition on metallic mirrors

In this work, amorphous hydrocarbon (a-C:H) film deposition on metallic mirrors was studied during working shots in tokamak T-10 and at exposure in Ar/CHD3/D2 dc magnetron discharge in a special laboratory high vacuum setup. Analysis of film composition (including hydrogen content) was carried out using nuclear physical methods. Thickness and optical parameters (refractive and extinction coefficients) of the films were estimated by ellipsometry. Laboratory films can be characterized as soft a-C:H films in comparison with hard tokamak films (ρ = 1.2 and 1.8 g/cm3, respectively). For the first one, a linear dependence of deposition rate on mirror temperature was observed in a wide temperature range. The addition of methane into initial Ar/D2 magnetron gas mixture leads to an increase of deposition rate. The data obtained should be taken into account to prevent hydrocarbon film formation on the surface of first mirrors in ITER.