Enhanced erosion of tungsten plasma-facing components subject to simultaneous heat pulses and deuterium plasma

When an ELM occurs in tokamaks, up to 30% of the pedestal energy can be deposited on the wall of the tokamak causing heating and material loss due to sublimation/evaporation and melt layer splashing of plasma-facing components (PFCs) and expansion of the ejected material into the plasma. A short-pulse laser system capable of reproducing the thermal load of an ELM heat pulse has been integrated into the existing PFC research program in PISCES, a laboratory facility capable of reproducing plasma-materials interactions expected during normal operation of large tokamaks. An Nd:YAG laser capable of delivering up to 1 J of energy over a 7 ns pulsewidth is used for the experiments. Laser heat pulse only, H+/D+ plasma only, and laser plus plasma experiments were conducted and initial results indicate enhanced erosion of tungsten exposed to simultaneous plasma and heat pulses, as compared to exposure to separate plasma-only or heat pulse-only conditions.