Tritium release from beryllium articles for use in fusion devices

Results obtained on radiation and magnetic field (MF) effects on tritium release at annealing of the beryllium pebbles from the EXOTIC-8-3/13 irradiation are presented in this study and compared with those for other irradiated beryllium materials. Abundance ratios of chemical forms of tritium in the EXOTIC-8-3/13 beryllium pebbles were determined: T2 – 65%, T0 – 23%, T+ – 12%. A complete detritiation of these pebbles was achieved at 1123 K for 240 min; MF of 2.35 T had no appreciable effect on the tritium release. At 991 K for 240 min, the degree of detritiation was 96.6% without MF; MF of 2.35 T decreased it to 86.7%. At 940 K for 47 min, the degree of detritiation was 60%, 5 MeV fast-electron radiation of 14 MGy/h increased it to 76%, but the simultaneous action of the fast-electron radiation and MF of 1.7 T increased it to 88%.