Behavior of Si impurity in Np–Am–MOX fuel irradiated in the experimental fast reactor Joyo

The irradiation behavior of uranium–plutonium mixed oxide fuels containing a large amount of silicon impurity was examined by post-irradiation examination. Influences of Si impurity on fuel restructuring and cladding attack were investigated in detail. Si impurity, along with Am, Pu and O were transported by spherical pores and cylindrical tubular pores to the fuel center during fuel restructuring of the Np–Am–MOX fuel, where a eutectic reaction of fuel and Si-rich inclusions occurred. After fuel restructuring of the Np–Am–MOX fuel, Si-rich inclusions without fuel constituents were agglomerated at fuel crack openings where shallow attacks on the inner wall of the cladding were seen. Such shallow attacks on the inner wall of the cladding were likewise observed near the location of fuel cracks in long-term steady-state irradiated MOX fuels. Evidence of these shallow attacks on the inner wall of the cladding remained after fuel restructuring in normal MOX fuel. However, grain boundary corrosion of the cladding inner wall at the opening of the fuel cracks was selective and was marked in MOX fuel at higher oxygen potential by the release of reactive fission products such as Cs and Te in comparison with other regions of cladding wall.