Tomographic atom probe characterization of the microstructure of a cold worked 316 austenitic stainless steel after neutron irradiation

For the first time, chemical analyses using Atom Probe Tomography were performed on a bolt made of cold worked 316 austenitic stainless steel, extracted from the internal structures of a pressurized water reactor after 17 years of reactor service. The irradiation temperature of these samples was 633 K and the irradiation dose was estimated to 12 dpa (7.81 × 1025 neutrons.m−2, E > 1 MeV). The samples were analysed with a laser assisted tomographic atom probe. These analyses have shown that neutron irradiation has a strong effect on the intragranular distribution of solute atoms. A high number density (6 × 1023 m−3) of Ni–Si enriched and Cr–Fe depleted clusters was detected after irradiation. Mo and P segregations at the interfaces of these clusters were also observed. Finally, Si enriched atmospheres were seen.