Thermochemical degradation of limestone aggregate concrete on exposure to sodium fire

Limestone aggregate concrete blocks were subjected to sodium fire conforming to a realistic scenario in order to qualify them as protective sacrificial layers over structural concrete flooring in liquid metal-cooled fast breeder reactors. Mid infrared absorption measurements were carried out on these sodium fire-exposed samples as a function of depth from the affected surface. Definite signatures of thermochemical degradation indicating dehydration and structural modification of the limestone concrete have been obtained. Control runs were carried out to delineate the thermal effects of sodium fires from that of the chemical interaction effects. Measurements on limestone aggregate samples treated with fused NaOH provided direct evidence of the exact mechanism of the sodium attack on concrete. The observed degradation effects were correlated to the mechanical strength of the concrete blocks and to the intensity of the sodium fire experienced.