Enhanced glass-forming ability of a Zr-based bulk metallic glass with yttrium doping

A significant enhancement in glass formation in a newly developed Zr51Cu20.7Ni12Al16.3 alloy has been achieved by yttrium doping. With just 0.5 at.% yttrium doping, the critical diameter of the as-cast alloys for glass formation has been increased from 3 mm to at least 10 mm. In the undoped, large-sized alloys, massive oxygen stabilized crystalline phases are observed but disappear in yttrium doped alloys. Very small amounts of stable α-Y2O3 phases found in the yttrium doped alloys, and their negligible effect on the metallic glasses’ properties, provide a superior solution to achieve metallic glasses with a high glass formability.