The influence of low-concentration γ-Fe2O3 magnetic nanoparticles in a poly(ether–b–ester) copolymer matrix on interfacial polarization and glass transition

A new poly(ester–b–ether) copolymer filled with magnetic γ-Fe2O3 nanoparticles of low concentration (0.1 and 0.3 wt%) has been synthesized, with poly(ethylene terephthalate) (PET) as a rigid segment and poly(tetraoxymethylene) (PTMO) as the flexible segment at the ratio of 50 wt%. The filler was used in the form of suspension or solid powder. The dielectric spectroscopy results for these materials, in a wide range of frequencies and temperatures, are presented and compared with similar results for a pure polymeric matrix. Two relaxation processes, α and β, have been observed clearly in all samples at about 253 K and 163 K, respectively. The α process was shifted towards the lower temperatures as the nanoparticle content increased, while the β-relaxation was unaffected by the doping. The interfacial polarization effect was observed in the samples with nanoparticles, less pronounced for the larger nanoparticles.