Structural characterization of phosphate glasses doped with silver

The present paper reports the influence of silver oxide addition on the local structure of 2P2O5 · CaO · 0.05ZnO glass matrix. The glass samples were investigated through several methods: X-ray powder diffraction (XRD), scanning electron microscopy (SEM), infrared absorption (FT-IR) and Raman scattering. The X-ray diffraction patterns confirm the vitreous character of these samples over the explored compositional range and the SEM pictures confirm this information. The phosphate structural units of the network former are assessed from FT-IR and Raman spectra as ultra-, meta-, pyro- and orthophosphate units. A slight structural depolymerization process of these phosphate-based glasses was evidenced for higher silver oxide content. In vitro behavior of the bulk glass sample with the highest silver oxide content was tested by immersion in simulated body fluid (SBF). X-ray diffraction and SEM measurements made on the SBF treated sample revealed growth of a crystalline phase on the surface sample.