Aging of a low molecular weight poly(methyl methacrylate)

Dielectric relaxation of a low molecular weight PMMA was measured in both the equilibrium and glassy states. The intense β process, due to motion of the pendant ester moiety, exhibits a change in T-dependence of both its relaxation time and dielectric strength at Tg, reflecting the coupling of this high frequency process to the backbone conformational changes underlying the α dynamics. Consequently, we can exploit the change in the properties of the β process during physical aging to quantify the α relaxation time and its T-dependence for glassy PMMA. The obtained values, τα > 104, are too long for direct measurement.