Mechanism of deleading of silicate glass by 0.5 N HNO3

Mechanism of removal of lead from silicate glass containing 68.5 wt% PbO by 0.5 N HNO3 was investigated by incorporation of the chemical-analyses/weight-loss data into shrinking-core model (SCM) and minimization of the difference. Scanning electron microscopy (SEM), emission spectrometry with inductively coupled plasma (ICP), X-ray diffraction (XRD) and energy dispersive X-ray analysis (EDS) were used to determine the compositional changes of the lead-silicate glass (LSG) samples. Dual inter-diffusion chemical reaction mechanisms having respective activation energies of 83.49 and 47.80 kJ/mol dominated the deleading process.