Synthesis and characterization of amorphous aluminosilicates prepared by sol–gel to encapsulate organic dyes

We synthesized via the sol–gel process three amorphous aluminosilicates having the stoichiometry of zeolite types A, X, and Y, respectively. The aluminosilicate, so-called SX, having the chemical composition of faujasite X, proved to be amorphous in the range 298 K up to 1273 K. At the higher temperature the sample begins to crystallize as nepheline. The anionic organic dye 1,2-dihydroxyanthraquinone (Alizarine, AL) was successfully encapsulated in the aluminosilicate matrix SX. Still, 7-α-D-glucopyranosil-9,10-dihydro-3,5,6,8-tetrahydroxy-7-methyl-9, 10 dioxanthracene carboxylic acid (carminic acid, CA) could only be deposited on the matrix surface. The adsorbents and the dye impregnated matrices were characterized using several techniques: Fourier Transform Infrared (FTIR) and Diffuse Reflectance Spectroscopies used to determine the hydroxylation as well as the adsorbed species, Small Angle X-ray Scattering (SAXS) to know the shape of the heterogeneities and the fractal dimension of each sample, nitrogen physisorption to measure the specific surface area and X-ray Diffraction (XRD) to identify the crystalline compounds present in the samples. Therefore, with these complementary techniques, the structure and the morphology of the samples were obtained.