Viscosity and kinetic fragility of alkaline earth zinc phosphate glasses

Kinetic fragility indices m and F1/2 as well as glass transition temperature Tg of alkaline earth zinc phosphate melts of molar composition 20 MO–30 ZnO–50 P2O5 (with M = Ba, Sr, Ca, Mg) were determined using viscometry and differential scanning calorimetry (DSC). Beam bending and concentric cylinder experiments were performed to measure the flow resistance in temperature ranges above glass transition and close to liquidus, respectively. Different upscan rates of DSC runs through the glass transition were used to correlate changes of the fictive temperature with kinetic fragility. Both methods revealed that glass transition temperature correlates negatively and kinetic fragility positively with the size of M. Metal cation mixing (M + Zn) led to a negative deviation from linearity for Tg, while exchanging M resulted in a linear dependence of Tg, if scaled with averaged charge-to-distance ratio. The fictive temperature method overestimated the compositional dependence of m by a ratio up to 1.9.