Investigation of glass forming ability in Ce–Al–Ni alloys

The compositional dependence of the glass forming ability (GFA), the correlation between their GFA and the GFA related parameters, and the thermal stability of the Ce–Al–Ni alloys were investigated. Rapidly quenched Ce65AlxNi35 − x (x = 2, 5, 10, 17, 20) and Ce70AlxNi30 − x (x = 2, 5, 10, 15, 20) ribbons were prepared by melt spinning, and their phase transformations were studied by X-ray diffraction (XRD), transmission electron microscopy (TEM) and differential scanning calorimetry (DSC). The experimental results indicated that the GFA of Ce65AlxNi35 − x (x = 2, 5, 10, 17, 20) and Ce70AlxNi30 − x (x = 2, 5, 10, 15, 20) alloys increased firstly and then decreased with the increasing of the Al content up to 20 at.%, respectively. It was found that only one parameter, F1, in evaluated currently available empirical GFA parameters searching for metallic glasses with a good GFA, can reflect the GFA of the Ce–Al–Ni alloys. It was indicated that the thermal stability of alloy with fully amorphous maybe lower than that of alloy with partial amorphous.