Fabrication of ceramic composite coatings using electrophoretic deposition, reaction bonding and low temperature sintering

We have developed a novel combination of electrophoretic deposition (EPD), reaction bonding and low temperature sintering techniques for the fabrication of yttria stablised zirconia (YSZ)/alumina composite coatings on Fecralloys. A mixture of ethanol and acetylacetone solvent was found to be an effective medium for YSZ and aluminium particle suspension. With the particle size of YSZ and aluminium being significantly reduced during ball milling. By using the EPD process, uniform green form coatings containing YSZ and aluminium particles were produced on Fecralloys. After oxidation of aluminium at 500°C and sintering at 1200°C, a dense and adherent YSZ/Al2O3 coating was produced. The presence of aluminium in the green form coatings not only contribute to the bonding between the coating and the metal substrate, but also compensate for the volume shrinkage of the coatings during sintering by the volume expansion arising from oxidation of aluminium to alumina.