Morphology of CuO through precipitation process under 2.45 GHz microwave irradiation

The morphology of CuO powders formed by a homogeneous precipitation process from aqueous copper precursor complex was investigated. The effect of 2.45 GHz microwave irradiation appeared in the characteristic morphology of the CuO microcrystal with comparison of an ordinal synthesis process. The crystallographic orientation of CuO microcrystals in the particle was examined by HRTEM. Using microwave irradiation, it was demonstrated that the morphology of the particles was kept through the decomposition of the precursor. Also the rapid transformation of a precursor to CuO in aqueous solution under microwave irradiation condition was discussed.