Plastic deformation of dense nanocrystalline yttrium oxide at elevated temperatures

Nanocrystalline yttrium oxide, Y2O3 with 110 nm average grain size was plastically deformed between 800 °C and 1100 °C by compression at different strain rates and by creep at different stresses. The onset temperature for plasticity was at 1000 °C. Yield stress was strongly temperature dependent and the strain hardening disappeared at 1100 °C. The polyhedral and equiaxed grain morphology were preserved in the deformed specimens. The experimentally measured and theoretically calculated stress exponent n = 2 was consistent with the plastic deformation by grain boundary sliding. Decrease in the grain size was consistent with decrease in the brittle to ductile transition temperature.