Microstructural evolution of YSZ electrolyte aerosol-deposited on porous NiO-YSZ

Dense, crack-free, ∼7.5 μm thick, 8 mol% yttria stabilized zirconia (YSZ) film was aerosol deposited on porous NiO-YSZ anode substrates at room temperature without additional high-temperature sintering. The films’ microstructures and gas permeability were observed after annealing at various temperatures. The dense, gas-tight film that was observed up to 1000 °C became porous at higher temperatures probably due to structural instability related to oxygen non-stoichiometry. A cell using such film as electrolyte showed an open cell voltage of 1.10 V and a maximum power density of 0.51 W/cm2 at 750 °C.