Abnormal variation of microwave dielectric properties in A/B site co-substituted (Ca1−0.3xLa0.2x)[(Mg1/3Ta2/3)1−xTix]O3 complex perovskite ceramics

A/B site co-substituted (Ca1−0.3xLa0.2x)[(Mg1/3Ta2/3)1−xTix]O3 ceramics (0.1 ≤ x ≤ 0.5) were prepared by solid state reaction and the structures, microstructures and dielectric properties were investigated. B site 1:2 cation ordering and oxygen octahedra tilting lead to monoclinic symmetry with space group P21/c for x = 0.1. For x above 0.1, the ordering was destroyed and the crystal structure became orthorhombic with space group Pbnm. The B site 1:2 cation ordering tended to be destroyed to form 1:1 ordering by the A site La3+ substitution. The dielectric constant increased linearly with increasing content of Ti4+ as the increasing second Jahn–Teller distortion enhanced the B site cation rattling. The temperature coefficient of resonant frequency and Qf values showed abnormal variations, which were refined to be caused by the increasing A site cation vacancy and diffused distribution of small size ordering domains respectively. Good combination of microwave dielectric properties was obtained at x = 0.5, where ɛr = 48, Qf = 21,000 GHz and τf = 2.2 ppm/°C.