Cellulose templating method for the preparation of La0.8Sr0.2Ga0.83Mg0.17O2.815 (LSGM) solid oxide electrolyte

La0.8Sr0.2Ga0.83Mg0.17O2.815 (LSGM) materials are synthesized with a fast and facile cellulose templating method for the first time and characterized by XRD, EIS, Archimedes method and SEM–EDS. LSGM powders with a phase purity of 91.7 mol% are obtained after the calcination at 1300 °C for 12 h. SEM–EDS results indicate possible decomposition and reconstruction of the LSGM phase due to the diffusion of Sr-rich species to the grain boundaries for the sample sintered at 1500 °C for 6 h. Maximum conductivity value is found to be 4.2 × 10−2 S cm−1 at 800 °C for the sample calcined at 1300 °C for 12 h and sintered at 1400 °C for 6 h. Phase purity, stability and relative density are the important factors for obtaining high performance LSGM electrolytes. Therefore, cellulose templating method is a promising candidate for the preparation of LSGM electrolytes.