Effect of recoating slurry compositions on the microstructure and properties of SiC reticulated porous ceramics

Silicon carbide reticulated porous ceramics (SiC RPCs) were fabricated by polymer sponge replica technique, followed by recoating with SiC slurries of two different sintering additives of MgO–Al2O3–SiO2 (Slurry 1) and polycarbosilane (Slurry 2). The sintering temperature of SiC RPCs recoated with Slurry 2 was 1100 °C, which was 200 °C lower than that for one recoated with Slurry 1. The prepared SiC RPCs exhibited homogeneous microstructure and contained pores with different sizes which was entrapped in the strut of SiC RPCs, small pores with diameter lower than 4 μm and large pores with diameter higher than 10 μm. Bending strength of SiC RPCs recoated with Slurry 1 was two times higher than that for the non-recoated samples, which was 1.88 MPa and was a little higher than that for one recoated with slurry 2. At the same time, high thermal shock resistance and high refractoriness were achieved for SiC RPCs recoated with Slurry 2.