Fabrication of porous silicon carbide ceramics with high porosity and high strength

Unique porous SiC ceramics with a honeycomb structure were fabricated by a sintering-decarburization process. In this new process, first a SiC ceramic bonded carbon (SiC/CBC) is sintered in vacuum by spark plasma sintering, and then carbon particles in SiC/CBC are volatized by heating in air at 1000 °C without shrinkage. The honeycomb structure has at least two different sizes of pores; ∼20 μm in size resulting from carbon removal; and smaller open pores of 2.1 μm remaining in the sintered SiC shell. The total porosity is around 70% and the bulk density is 0.93 mg/m3. The bending and compressive strengths are 26 MPa, and 105 MPa, respectively.