Fracture mechanics evaluation of cast duplex stainless steel after thermal aging

For the primary coolant piping of PWRs in Japan, cast duplex stainless ateci, which is excellent in terms of strength, corrosion resistance and weldability, has conventionally been used. Cast duplex slainless steel contains the ferrite phase in the austenite matrix, and thermal aging after long-term service is known to decrease fracture toughness. Therefore, we evaluated the integrity of the primary coolant piping for an initial PWR plant in Japan by means of elastic plastic fracture mechanics. The evaluation results show that the crack will not grow into an unstable fracture and the integrity of the piping will be secure, even when such through-wall crack length is assumed to be as large as the fatigue crack length grown for a service period of up to 60 years. © 1999 Elsevier Science S.A. All rights reserved.